Al2O3 dission na-ewu ewu carper (c15715, C15725, C15760)
* Saịlị ewusi ike ọla kọpa nwere ezigbo nguzogide okpomọkụ na-eme ka ọ dị elu na mgbakwunye na-eme ihe na-akpata ikuku.
* Ike na-arụ ọrụ dị elu na omume dị elu na-arụ ọrụ ọla kọpa na-eme ka ebe a na-ebubata ya n'ihi arụmọrụ arụmọrụ dị elu.
* A na-enyocha ya dịka jaiangsu elu-teta (maka klaasị ọhụrụ) na 2013
* Enyerela ụlọ ọrụ abụọ ihe omimi.
1. Ihe mejupụtara kemịkalụ al2o3 na-eme ka ike ọla kọpa
| Mogosi | Cu + ag | Al2O3 | Ala | Ob | P | Fe | Pb |
| C15715 | ≥99.45 | 0.25-0.32 | ≤0.03 | ≤0.015 | ≤0.003 | ≤0.01 | ≤0.01 |
| C15725 | ≥99.25 | 0.43-0.51 | ≤0.03 | ≤0.015 | ≤0.003 | ≤0.01 | ≤0.01 |
| C15760 | ≥98.55 | 0.10-0.20 | ≤0.03 | ≤0.015 | ≤0.003 | ≤0.01 | ≤0.01 |
| aAl nke dị n'ụdị ndị ọzọ na-abụghị al2O3 | |||||||
| bO nke dị na mpempe akwụkwọ na-abụghị al2O3 | |||||||
2
| Dayameta | Na-agbanwe agbanwe | Okpurukpu | Dayameta | ||||
| 50-100 | ± 0.03 | ≤100 | > 100-200 | > 200-300 | > 300-400 | > 400-600 | |
| > 100-200 | ± 0.04 | Na-ekwe omume ichefu ọkpụrụkpụ | |||||
| > 200-300 | ± 0.05 | 10-20 | ± 0.30 | ± 0.35 | ± 0.40 | ± 0.45 | ± 0.50 |
| > 300-400 | ± 0.06 | > 20-30 | ± 0.35 | ± 0.40 | ± 0.45 | ± 0.50 | ± 0,55 |
3
| Mogosi | Onodu | Tensile ike rm (MPA) | Mpempe akwụkwọ plastind akọwapụtara nke ọma RP0.2 (MPA) |
| Rockwell siri ike hrb | Nnọkọ ụda olu (Ω * mm2 / m) | Eletriki echiche (IACs,%) | Eletriki echiche (Ms / m) |
| C15715 | H04 | ≥477 | ≥407 | ≥14 | ≥63 | ≤0.01874 | ≥92 | ≥53.4 |
| C15725 | H04 | ≥483 | ≥448 | ≥12 | ≥77 | ≤0.01937 | ≥89 | ≥51.6 |
| C15760 | H04 | ≥5552 | ≥517 | ≥10 | ≥83 | ≤0.02210 | ≥78 | ≥45.2 |
4.
A na-ejikarị ya maka ndị na-agba aja aja