Elu nkenke Beryllium ọla kọpa Tube C17200
Mepụtara ọjà beryllium ọla kọpa na-enweghị ntụpọ maka ọdụ ọdụ 5G.Ka ọ dị ugbu a, ọ bụ naanị onye na-emepụta ụlọ nke beryllium ọla kọpa na-enweghị ntụpọ nke nwere ezigbo mma na oke ọkọnọ.The elu dayameta nwere ike ịbụ 1.0 ~ 25mm na mgbidi ọkpụrụkpụ bụ 0.08 ~ 6mm , The ndidi nwere ike ịbụ ezi na ± 0.01mm.Ụlọ ọrụ na-enye mgbe niile nke 2.0 * 1.6 2.0 * 1.8 3.5 * 3.2 3.95 * 3.65 na ndị ọzọ dị elu beryllium ọla kọpa enweghị nkebi ọkpọkọ ejiriwo n'ọtụtụ ebe na 5G base station akụrụngwa dị ka Huawei, ZTE na Nokia.
1. Chemical mejupụtara nke C17200 Tube
| Nlereanya | Be | Ni + Co | Ni + Co + Fe | Al | Si | Cu |
| C17200 | 1.8-2.0 | ≥0.20 | ≤0.6 | ≤0.2 | ≤0.2 | Nke fọdụrụ |
2. Njirimara anụ ahụ nke C17200 Tube
| Steeti | Ike ọdụdọ | Mpụta Ike | Rockwell Hardness | 4×DA | Igwe ọkụ eletrik | ||
| Mpa | 0.2% ,Mpa | B | Ogologo oge | IACS,% | |||
|
|
|
| min% |
| |||
| TB00 | Ọgwụgwọ Okpomọkụ Ngwọta siri ike (A) | 410-590 | 140 | 45-85 | 20 | - | |
| TD04 | Hardening State (H) | Dayameta 10mm | 620-900 |
| 88-103 |
|
|
|
|
|
| |||||
| Dayameta: 10-25mm | 620-860 |
| 88-102 | 8 | > 17 | ||
| Dayameta 25-75mm | 590-830 | 520 | 88-101 |
|
| ||
| Steeti | Ike ọdụdọ | Mpụta Ike | Rockwell Hardness | 4×DB | Igwe ọkụ eletrik | ||
| Mpa | 0.2% ,Mpa | B | Ogologo oge | ||||
|
|
|
| min% | ||||
| TF00 | Ọgwụgwọ ọkụ nke nkwụnye ego (AT) | 1140-1380 | 1000 | 36-42 | 4 | - | |
| TH04 | Ịkwụsi ike & Nkwụnye Ọkụ Ọkụ nke Mmebe(HT) | 1240-1580 | 1070 | 38-44 | 2 | > 22 | |
3. Njirimara nke C17200 Tube
Akwa ike, elu conductivity, elu ike ọgwụgwụ, elu eyi iguzogide, na-abụghị magnetik
4. Ngwa nke C17200 Tube
A na-ejikarị ya maka ọdụ ọdụ 5G, njikọ njikọ coaxial, tube fotomultiplier, ngwa nkenke dị elu, ikuku agha.